Refill PLA Matte HS Bordeaux – Azurefilm
View
Maintain stock, refill and create with Azurefilm’s refillable PLA Matte HS Bordeaux filament.
PLA Matte HS is designed for anyone looking for a matte and aesthetic finish for their parts. The matte surface of this filament hides the layer lines well, further enhancing the appearance of the printed object. PLA Matte HS is easy to print, has excellent first layer adhesion and can be used for printing at speeds up to 500 mm/s.
The PLA Matte HS fillers have exactly the same properties as the PLA Matte HS fillers. These filaments are an environmentally friendly choice that offers reliable performance and consistent results.
Recommendations for printing
- For best results, print at 205-255°C*.
- You don’t need a heated bed, but we recommend pre-heating your print table to 50-60°C.
- Use a glass bed, PEI sheet, Kapton or blue tape for the build platform with 3Dlac spray or EcoFixy adhesive.
*The ideal temperature may vary when using different printers.
| Standard | Value | Unit | |
|---|---|---|---|
| Print Temperature: | AF | 205-225 | °C |
| Pad Temperature: | AF | 60 | °C |
| Print speed: | AF | 300-500 | mm/s |
| Cooling: | AF | 100 | % |
| Pad surface: | / | (Textured) PEI, glass bed, BUILDTAK | / |
Azurefilm’s PLA Matte HS charging filaments are fully compatible with AzureFilm base spool – the only spool you will ever need. By using this reusable spool, you can join us in reducing waste and minimizing environmental impact.
The AzureFilm Master Spool is our reusable spool that provides a sustainable and cost-effective 3D printing solution. The spool is a set of two reusable discs made using the injection molding method. This ensures the high durability and precision of the spool.
By purchasing and reusing our Master Spool, you are contributing to a cleaner environment while enjoying a reliable and easy-to-use product compatible with most 3D printers.
Applications
The PLA Matte HS collection is ideal for beginners as it is easy to print. Despite its ease of use, PLA Matte HS has improved aesthetic properties compared to regular PLA, making it suitable for a variety of applications such as decorations.
Consistent matt surface finish
The filaments of the Matte collection have a characteristic matt surface that allows the lines of the layers to be hidden. Try PLA Matte HS and enjoy the professional look of your details and patterns.
High-speed printing
The ability to print at speeds of up to 500 mm/s allows you to create quickly and efficiently. The print speed does not affect the mechanical properties of the filament and does not alter the matte appearance of the final object.
Less visible layer lines
The PLA Matte HS collection is specifically designed to provide less visibility of layer lines – a common challenge in 3D printing. This feature is particularly useful for applications where aesthetics are paramount. The reduced need for post-processing enables the creation of beautiful architectural models, decorations and prototypes.
Excellent adhesion of the first layer
Adhesion to the print bed is critical as it affects print stability and quality. PLA Matte HS excels in this area as the parts adhere well to the build plate throughout the printing process. This also reduces the need for additional adhesives such as glues, tapes or sprays that can complicate the assembly and cleaning process.
Product storage
We recommend storing the filaments in a cool, dry, enclosed area with a silica pack away from UV light.
Characteristics and properties
| Standard | XY Value | XZ Value | ZX Value | Unit | |
|---|---|---|---|---|---|
| Tensile strength: | ISO 527-2 | 42.8 | 44.2 | 21.7 | MPa |
| Yield strength: | ISO 527-2 | 32.9 | 32.8 | / | MPa |
| Tensile Module: | ISO 527-2 | 3800 | 3800 | 3200 | MPa |
| Deformation in mining: | ISO 527-2 | 4.1 | 3.6 | 0.8 | % |
| Bending strength: | ISO 178 | 81.8 | 83 | 52.7 | MPa |
| Bending mode: | ISO 178 | 4500 | 4500 | 4000 | MPa |
| Impact Force: | ISO 179 | 6 | / | / | kJ/m² |
You can access the technical specification here.