Panchroma™ CoPE: High-speed, high-quality copolyester for easy printing
Exceptional surface quality and easy handling
Panchroma™ CoPE is a copolyester-based filament designed for seamless printing and an exceptionally smooth, high quality surface. Its advanced formulation significantly improves the printability of bridges and overhangs, enabling reliable, high-speed printing up to 400 mm/s. .
Panchroma™ CoPE is a copolyester-based filament designed for seamless printing and an exceptionally smooth, high quality surface. Its advanced formulation significantly improves the printability of bridges and overhangs, enabling reliable, high-speed printing up to 400 mm/s. .
Superior bed adhesion and important handling tips
This material offers excellent bed adhesion, which prevents warping even on difficult-to-print patterns. However, adhesion can be so strong that the use of a release agent is recommended for easier part removal. Avoid using textured PEI plates without additional adhesive as adhesion can be excessive. For easiest separation, allow prints to cool completely to room temperature.
This material offers excellent bed adhesion, which prevents warping even on difficult-to-print patterns. However, adhesion can be so strong that the use of a release agent is recommended for easier part removal. Avoid using textured PEI plates without additional adhesive as adhesion can be excessive. For easiest separation, allow prints to cool completely to room temperature.
Specific Compatibility
Panchroma™ CoPE does not bond well to standard PLA, making it unsuitable for multi-material printing combining Panchroma’s PLA-based effects. However, this poor adhesion is an advantage when using CoPE as a support material (breakaway support) for PLA patterns – it allows clean and easy removal of supports.
Panchroma™ CoPE does not bond well to standard PLA, making it unsuitable for multi-material printing combining Panchroma’s PLA-based effects. However, this poor adhesion is an advantage when using CoPE as a support material (breakaway support) for PLA patterns – it allows clean and easy removal of supports.
Why choose Panchroma™ CoPE?
Choose this material for projects that require fast and reliable printing, excellent surface quality and strong adhesion – especially for complex geometries or when easily separable supports are required.
Choose this material for projects that require fast and reliable printing, excellent surface quality and strong adhesion – especially for complex geometries or when easily separable supports are required.
Technical parameters for printing
These settings are optimized for maximum speed and quality:
- Nozzle temperature: 190°C – 230°C
- Bed temperature: 25°C – 60°C
- Maximum print speed: Up to 400 mm/s
- Cooling fan: ON
- Drying settings: 55°C for 6 hours (if the material has absorbed moisture)
- Retraction (Direct Drive): Distance 1 mm, Speed 20 mm/s
- Retraction (Bowden): Distance 3 mm, Speed 40 mm/s
Mechanical properties (TDS “Regular”)
Values are for X-Y orientation under standard conditions:
- Tensile Strength: 51.6 ± 0.3 MPa
- Young’s Modulus: 2515 ± 71 MPa
- Impact Strength (Charpy Impact): 2.9 ± 0.1 kJ/m²
- Vicat Softening Temperature: 65.5°C
- Glass Transition Temperature: 58.2°C